Stereolithography of SiOC Polymer?Derived Ceramics Filled with SiC Micronwhiskers

3D printing of pre?ceramic polymers can broaden applications with complex geometries. A SiC reinforced SiOC polymer?derived ceramic is printed and characterized via XRD, SEM, and hardness testing.Due to complicated manufacturing methods and lack of machinability, the use of engineering ceramics is limited by the manufacturing processes used to fabricate parts with intricate geometries. The 3D printing of polymers that can be pyrolyzed into functional ceramics has recently been used to significantly expand the range of geometries that can be manufactured, but large shrinkage during pyrolysis has the potential to lead to cracking. In this work, a method to additively manufacture particle?reinforced ceramic matrix composites is described. Specifically, stereolithography is used to crosslink a resin comprised of acrylate and vinyl?functionalized siloxane oligomers with dispersed SiC whiskers. After crosslinking, the part is pyrolyzed to amorphous SiOC while the SiC whiskers remain unaffected. Composite ceramics shrink 37% while unreinforced parts shrink 42%; this significant reduction in shrinkage improves part stability. Importantly, these ceramic matrix composites contain no visible porosity nor cracking on the microstructural level. With the introduction of SiC, hardness increases from 10.8 to 12.1?GPa and density decreases from 2.99 to 2.86?g?cm?3. Finally, printed ceramic porous structures, gears, and components for turbine blades are demonstrated. Applying stereolithographic techniques to ceramic matrix composites, this work may improve processing and properties of ceramics for applications that require complex geometries.

» Author: Stephan A. Brinckmann, Niranjan Patra, Jia Yao, Taylor H. Ware, Carl P. Frick, Ray S. Fertig

» Reference: doi:10.1002/adem.201800593

» Publication Date: 21/09/2018

» More Information

« Go to Technological Watch



AIMPLAS - Instituto Tecnológico del Plástico | C/ Gustave Eiffel, 4 (Valčncia Parc Tecnolňgic) | 46980 - PATERNA (Valencia) - SPAIN
(+34) 96 136 60 40
ecogelcronos@aimplas.es

This project has received funding from the European Union Seventh Framework Programme (FP7/2007-2013) under grant agreement n° [609203].

The sole responsibility for the content of this website lies with the authors. It does not necessarily reflect the opinion of the EC. The EC is not responsible for any use that may be made of the information contained therein.