PANI coated microporous graphene fiber capable of subjecting to external mechanical deformation for high performance flexible supercapacitors

Graphene based composites have been recognized as one of the most important classes of free-standing electrodes for supercapacitors. Herein, one-dimensional microporous graphene oxide fiber (MG) was designed with polystyrene sulfonate (PSS) microspheres as hard-template through a simple mass production method. The MG fiber exhibited outstanding flexibility and excellent tensile strength of 183.7 MPa. Then the polyaniline (PANI) coated microporous graphene (MGP) fibers were prepared by in-situ electropolymerization of aniline. Benefiting from the unique microporous structure, the optimized MGP fiber electrode exhibited remarkable electrochemical characteristics, such as highest specific capacitance of 36.95 mF/cm at current density of 0.25 mA/cm (204.2 F/cm3 at current density of 1.38 A/cm3), as well as excellent capacitance retention of 96.31% after 2000 cyclic voltammetry cycles. More than that, the MGP fiber electrode remained high retention rate of its initial specific capacitance even under tensile stress or bending, indicating its good tolerance to external damage.

» Author: Dong Liu, Juanli Liu, Qi Wang, Pengcheng Du, Wenli Wei, Peng Liu

» Reference: 10.1016/j.carbon.2018.10.098

» Publication Date: 05/11/2018

» More Information

« Go to Technological Watch



AIMPLAS - Instituto Tecnológico del Plástico | C/ Gustave Eiffel, 4 (Valčncia Parc Tecnolňgic) | 46980 - PATERNA (Valencia) - SPAIN
(+34) 96 136 60 40
ecogelcronos@aimplas.es

This project has received funding from the European Union Seventh Framework Programme (FP7/2007-2013) under grant agreement n° [609203].

The sole responsibility for the content of this website lies with the authors. It does not necessarily reflect the opinion of the EC. The EC is not responsible for any use that may be made of the information contained therein.