Performance study of ultrasonic assisted processing of CNT nanopaper/solventless epoxy composite

This work presents an innovative ultrasonic-assisted process for the fast infiltration of solventless epoxy into carbon nanotube (CNT) nanopaper (NP) (50 ?m thick thin film) to fabricate prepregs and composites. The effect of process parameters including: ultrasonic time (infiltration time), ultrasonic amplitude, pressure, and mold temperature on the resin impregnation quality and composite mechanical properties were evaluated. Nanopapers made of multi wall carbon nanotube (MWNT) or single wall carbon nanotube (SWNT) were used in this work. Homogeneous resin impregnation was achieved in the MWNT NP/epoxy composite with 30.5?wt. % MWNT loading. For coating applications, the MWNT NP/epoxy composite showed 167% improvement in sand erosion resistance compared to glass fiber/epoxy composite. NPs with different MWNT wt. % and SWNT wt. % were fabricated. Although non-uniform resin impregnation was observed in SWNT NP/epoxy composites, there was still 142% improvement in tensile strength compared to pure epoxy due to the rigid SWNT NP structure. The EMI shielding of SWNT NP reached 57?dB, which was higher than commercial carbon fiber preform (51?dB). The CNT NP/epoxy composites offer multi-functional properties, and demonstrate promising coating applications in wind energy, automotive and sporting goods industries.

» Author: Dan Zhang, Maria G. Villarreal, Eusebio Cabrera, Avraham Benatar, L. James Lee, Jose M. Castro

» Reference: 10.1016/j.compositesb.2018.10.012

» Publication Date: 05/10/2018

» More Information

« Go to Technological Watch



AIMPLAS - Instituto Tecnológico del Plástico | C/ Gustave Eiffel, 4 (Valčncia Parc Tecnolňgic) | 46980 - PATERNA (Valencia) - SPAIN
(+34) 96 136 60 40
ecogelcronos@aimplas.es

This project has received funding from the European Union Seventh Framework Programme (FP7/2007-2013) under grant agreement n° [609203].

The sole responsibility for the content of this website lies with the authors. It does not necessarily reflect the opinion of the EC. The EC is not responsible for any use that may be made of the information contained therein.