Preparation and Corrosion Behaviour Studies of Chemically Bonded Phosphate Ceramic Coating Reinforced with Modified Multi?walled Carbon Nanotubes (MWCNTs)

To improve the corrosion resistance of the chemically bonded phosphate ceramic coating, the MWCNTs are selected as the reinforcement after the modification. Through the analysis of TEM, Raman, XRD and FTIR, it can be shown that MWCNTs are modified with carboxyl groups and the surfactant after treatment, and show good dispersion. In addition, the electrochemical experiments were carried out with 3.5wt% NaCl solution to investigate the corrosion behavior of the coatings. The results suggest that the corrosion resistance of coatings is improved with the introduction of MWCNTs and the corrosion resistance increases with the increase of MWCNTs. Besides, the corrosion mechanism of MWCNTs reinforced coating corrosion resistance was also investigated based on the corrosion behaviour and microstructural characterizations. The gel strength is improved with the addition of MWCNTs because of its strong strength, which can prevent crack occurring and form the bridge when crack happens. Therefore, H2O, O2, and Cl? can be prevented from reaching to the substrate, which leads to good corrosion resistance.This article is protected by copyright. All rights reserved.

» Author: Rongli Xu , Da Bian , Thirumala Vasu Aradhyula , Chavali Murthy , Yongwu Zhao

» Reference: doi:10.1111/ijac.13107

» Publication Date: 08/09/2018

» More Information

« Go to Technological Watch



AIMPLAS - Instituto Tecnológico del Plástico | C/ Gustave Eiffel, 4 (Valčncia Parc Tecnolňgic) | 46980 - PATERNA (Valencia) - SPAIN
(+34) 96 136 60 40
ecogelcronos@aimplas.es

This project has received funding from the European Union Seventh Framework Programme (FP7/2007-2013) under grant agreement n° [609203].

The sole responsibility for the content of this website lies with the authors. It does not necessarily reflect the opinion of the EC. The EC is not responsible for any use that may be made of the information contained therein.