LPCVD-based SiO2/SiC multi-layers coating on graphite for improved anti-oxidation at wide-ranged temperatures

A novel SiO2/SiC multilayer coating was prepared on graphite by low-pressure chemical vapor deposition (LPCVD) with the aim of enhancing oxidation resistance at wide-ranged elevated temperatures. The anti-oxidation tests were performed at 1000 °C and 1500?°C in ambient air. The results showed that oxidation of SiO2/SiC multilayer coating was a continuous weight gain process, compared to the fast weight-loss of single SiC coated specimens. The final weight gains of SiO2/SiC coated specimens after oxidation at 1000?°C and 1500?°C for 120?h in ambient air are 0.116 mg/cm2 and 0.225?mg/cm2, respectively. The superior anti-oxidation performance of SiO2/SiC multilayer coating is ascribed to the intact combination between layers and excellent self-healing ability of SiO2 at elevated temperature.

» Author: Yang Li, Wu Liang, Yuan Shi, Wei Zhou

» Reference: Composites Part B: Engineering, Volume 146

» Publication Date: 01/08/2018

» More Information

« Go to Technological Watch



AIMPLAS - Instituto Tecnológico del Plástico | C/ Gustave Eiffel, 4 (Valčncia Parc Tecnolňgic) | 46980 - PATERNA (Valencia) - SPAIN
(+34) 96 136 60 40
ecogelcronos@aimplas.es

This project has received funding from the European Union Seventh Framework Programme (FP7/2007-2013) under grant agreement n° [609203].

The sole responsibility for the content of this website lies with the authors. It does not necessarily reflect the opinion of the EC. The EC is not responsible for any use that may be made of the information contained therein.