Bio-based episulfide composed of cardanol/cardol for anti-corrosion coating applications

Bio-based materials from Cardanol/cardol with episulfide group (CCES) and epoxy group (CCEO) were synthesized and further blended with commercial bisphenol-A diglycidyl ether type epoxy resin (DGEBA) for anti-corrosion coating application. The curing behavior of CCEO and CCES confirmed that episulfide exhibited a faster curing rate and higher curing conversion than epoxide. Anticorrosion properties of composite system CCEO/CCES and DGEBA were also carried out. Equilibrium water content of CCES-DGEBA blend was much lower than neat DGEBA and CCEO-DGEBA composite system in water absorption test, which met agreement with that CCES-DGEBA blend system revealed better adhesive to the metal compared with DGEBA and CCEO-DGEBA blend in lap sheer strength assessment. Further, CCES-DGEBA blend with 20 wt% of CCES exhibited optimized performance in corrosion resistance as it possessed the higher impedance modulus at low frequencies in EIS bode plots, lowest corrosion current and the highest corrosion voltage in Tafel test.

» Author: Jie Lv, Zhuoyu Liu, Jie Zhang, Jizhen Huo, Yingfeng Yu

» Reference: Polymer

» More Information

« Go to Technological Watch



AIMPLAS - Instituto Tecnológico del Plástico | C/ Gustave Eiffel, 4 (Valčncia Parc Tecnolňgic) | 46980 - PATERNA (Valencia) - SPAIN
(+34) 96 136 60 40
ecogelcronos@aimplas.es

This project has received funding from the European Union Seventh Framework Programme (FP7/2007-2013) under grant agreement n° [609203].

The sole responsibility for the content of this website lies with the authors. It does not necessarily reflect the opinion of the EC. The EC is not responsible for any use that may be made of the information contained therein.